TEROSON PU 9100 WHITE IN 20 KG DRUM

(Code: 02-10417-02)

Data Sheet
409.79 €
Add to cart
TEROSON PU 9100 WHITE IN 20 KG DRUM

TEROSON PU 9100 WHITE - DRUM 20 KG



Teroson PU 9100 is a gun-grade, one component adhesive/sealant based on polyurethane.



Characteristics
  • Cures by reaction with moisture to a soft elastic product
  • The skin formation and curing times are dependent on humidity and temperature
  • The curing time also depends on joint depth
  • By increasing the temperature and moisture these times can be reduced
  • Low temperature as well as low moisture retard the process

Teroson PU 9100 exhibits the following properties:
  • good adhesion to painted surfaces, many metals and plastics without primer
  • can be overpainted
  • sag resistant
  • high curing speed
  • excellent elasticity


Application

Teroson PU 9100 is used for elastic sealing and bonding, particularly seam sealing and sealing of narrow joints in the following areas:
  • vehicle and vehicle body manufacture
  • railway carriage and container manufacture
  • vehicle body build-ups
  • ship and boat building
  • metal and sheet metal manufacture
  • bonding and sealing of flange connections
  • bonding of customising parts like spoilers and trim rails

Temporary fixation of the joint with adhesive tapes or spacers is advised until the adhesive/sealant has completely cured.
Teroson PU 9100 offers the important advantage that both bonding and sealing functions can be achieved with one product. Teroson PU 9100 is not generally suitable for constructive bonding.

Technical characteristics
  • Colour : white
  • Odour : aromatic (no smell after curing)
  • Consistency : paste, brushable – can also be applied by spatula
  • Density : approx. 1.20 g/cm3
  • Sag resistance: very good
  • Curing mechanism: moisture curing
  • Skin formation time (DIN 50014 standard climate: 23°C, 50 % rh): approx. 20–45 mins
  • Cure rate (DIN 50014 standard climate: 23°C, 50 % rh): approx. 4 mm/24 h
  • Shore-A-hardness (DIN 53505): approx. 45
  • Tensile strength (DIN 53504): approx. 1.7 MPa
  • Elongation to break (DIN 53504): approx. 350 %
  • Tear resistance (DIN 53515): approx. 11 N/mm
  • G-modulus: approx. 0.65 MPa
  • Application temperature: 5°C to 35°C
  • In service temperature range: -40°C to 90°C