Sikafast 5215 NT is a fast curing 2-C structural adhesive, designed for glass bonding.



Characteristics
  • Strength development within minutes after application
  • Adhesion to a wide range of metals and plastics as well as glass with no or only limited substrate preparation
  • High strength
  • Gap filling, allowing for manufacturing tolerances (up to 3 mm)
  • Flexible, Vibration damping
  • Solvent and acid-free
  • Easy mixing
  • Low odour
  • Approved NSF R2 (accidental food contact)


Application
  • New generation of fast curing, flexible adhesives designed to substitute welding, riveting, clinching and other, mechanical fastening techniques
  • Suitable for structural and semi-structural bonding on a wide range of substrates in the assembly and trim shop, for high strength fastening of concealed joints on different types of substrates including glass, top coats, plastics, etc.


Technical characteristics

Composant A SikaFast-5215 NT
  • Colour : White
  • Density (CQP 006-4) : 1,15 kg/l approx.
Composant B SikaFast-5200
  • Colour : Black
  • Density (CQP 006-4) : 1,5 kg/l approx.
Mixture (A+B)
  • Chemical base : Acrylic
  • Colour : Grey
  • Curing mechanism : Polymerisation
  • Density mixed (calculated) : 1,19 kg/l approx.
  • Mixing ratio
            by volume : 10 : 1
            by weight : 10 : 1,3
  • Consistency : Thixotropic paste
  • Application temperature : +5°C to +40°C
  • Open time at 23°C (73°F) / 50% r.h. (CQP 526-2) : 5 min. approx.
  • Shore-A-hardness (CQP 023-1 / ISO 868) : 90 approx.
  • Shore-D-hardness (CQP 023-1 / ISO 868) : 50 approx.
  • Tensile stress at 23°C (73°F) / 50% r.h. (CQP 036-1 / ISO 37) : 10 MPa approx.
  • Elongation at break at 23°C (73°F) / 50% r.h. (CQP 036-1 / ISO 37) : 200% approx.
  • E-Module at 23°C (73°F) / 50% r.h. (CQP 036-1 / ISO 37) :; 250 MPa approx.
  • Tensile-shear strength at 23°C (73°F) / 50% r.h.(CQP 046-6 / ISO 4587) : 10 MPa approx.
  • Glass transition temperature (CQP 509-1 / ISO 6721-2) : +60°C approx.
  • Service temperature : -40°C to +80°C