TEROSON PU 8630 HLMC SET IN KIT

TEROSON PU 8630 HLMC SET



Teroson PU 8630 HMLC SET is a bi-component polyurethane adhesive with high shear modulus and low conductivity.



Characteristics
The direct glazing adhesive is outstanding for the following properties:
  • Very good sag resistance
  • High elastic and shear strength, even after aging
  • Very low conductivity
  • Good adhesion to the remaining material
  • Excellent adhesion to glass, glass with the ceramic coating, encapsulation and to painted surfaces, in connection with primer/activator
  • High UV resistance in connection with primer/activator
  • High shear modulus
  • Easy to use ( application with battery gun / 1C pneumatic gun)


Application

Teroson PU 8630 HMLC is used for the bonding of front, rear and side screens to the body of motor-, utility-, special- and rail vehicles.

Technical characteristics
  • Colour : black
  • Odour : weak
  • Consistency : smooth, sag-resistant, pasty
  • Density : approx. 1.2 g/cm3
  • Solids : 100%
  • Shore-A-hardness (DIN 53505): approx. 60
  • Tensile strength (DIN 53504): approx. 9.5 MPa
  • Stress (DIN 53504): approx. 5.7 MPa at 100 % elongation
  • Shear modulus (DIN 54451): approx. 3.0 MPa
  • Elongation to break (DIN 53504): approx. 370 %
  • Shear strength (thickness 5mm, 56 MPa (fully cured) based on DIN EN 1465) :
        approx. 4 to 5 MPa (fully cured)
  • Specific forward resistance (ASTM D 257-99 / DIN IEC 60093) : approx. 11010 ω cm
  • Volume change (DIN 52451) : < 1 %
  • Glazing time* : max. 25 mins
  • Material application temperature : +60C to +70C
  • In service temperature range : -40C to +90C
        short exposure (up to 1 hr.) : +120C
* period of time between beginning of material application until inserting of the pane